Finngard 500 - Protective Coating for Concrete

Finngard 500
DESCRIPTION Water-borne, alkali-resistant, hydrophobic, acrylate coating protecting the concrete against humidity and carbonation. Maximum grain size approx. 0.5 mm.
PRODUCT FEATURES For coating concrete structures, mineral-based building boards, and rendered concrete surfaces. 
RECOMMENDED USES Residential, business and industrial buildings, warehouses etc.

TECHNICAL DATA
  The paint is suitable for exterior walls The paint is full-matt The paint is water-borne Tool: roller Tool: spray
The coverage of the paint on rough surfaces
0.4
The coverage of the paint on smooth surfaces
0.5
Base paints FFA and FFC
Colour Range Tikkurila Façade colour card
Gloss grade Full-matt
Coverage 0.4-0.5 kg/m2 on one coat. Coverage depends on the roughness and porosity of the surface to be coated as well as painting method and conditions. 
Can sizes 18 l
Thinner Water
Application method Roller, brush or spray with elevated tank or high pressure application (min. nozzle size 0.043''or 1.09 mm, spray angel 60º).
Drying time at 23°C and 50% relative air humidity Recoatable after 12 hours.
Water vapour resistance (EN ISO 7783-2) sD ≤ 0,5 m
Water permeability (EN 1062-3)

w < 0.1 kg/m² ∙ h0,5  

Adhesive strength (ISO 4624) > 1.5 N/mm².
Permeability to CO2 (EN 1062-6) sD > 200 m
Weather resistance Good, also in maritime and industrial climate. Prevents the penetration of rain and splashes into the construction. Allows water to come through from inside as a vapour
Solids volume Approx. 50 %.
Density Approx. 1.4 kg/l, ISO 2811
Storage Protect from frost. The temperature of the product or the container may not exceed +35°C. May not be stored in the sunshine, not even under tarpaulin. Tinted or paint in poorly sealed or partly filled can does not stand long-term storage.

APPLICATION DETAILS
Application conditions The surface to be treated has to be dry, the temperature of the air at least +5 °C, and the relative humidity of the air below 80 %. Do not paint under strong sunlight.
Preparation New untreated surfaces
The substrate has to be sufficiently dried and hardened before treatment. For example painting conditions and thickness of the plaster layer affect the drying and hardening time.

Clean the surfaces from dirt, dust and salts. Wash mouldy, mossy etc. surfaces using Tikkurila Mould Removal according to instructions. Very porous concrete surfaces are recommended to be levelled with Finnseco Polytop Finishing Mortar or Finnseco Levelling Mortar.

Previously painted surfaces
Clean the surfaces from dirt, dust and salts. Wash mouldy, mossy etc. surfaces using Tikkurila Mould Removal according to instructions. Remove flaking or poorly attached paint coats from previously painted surfaces. Choose the method of removal according to solidity of the substrate and type of paint to be removed (e.g. steel-brushing, high-pressure washing with hot water or water-sand blasting). Carry out necessary concrete repair, patching and filling using the Finnseco products as instructed.
Priming The need for priming is defined case by case. Chalking substrate is recommended to be primed with Tikkurila Hydrosol Primer. Water-repelling properties of the substrate can be improved with Tikkurila Silicone Primer. Follow instructions in the data sheet.
Application Apply two coats. The paint can be thinned up to 5 % with water for priming, if necessary. Finish with unthinned paint.

Note !
Stir Finngard 500 well before use. Reserve enough paint from the same batch for one uniform surface, to avoid possible colour differences. Should you need to use two different production batches, paint the joints with a solution of 1 part of old batch and 1 part of new batch. Make sure that this joint is in as inconspicuous point as possible.

The paint should be applied without interruptions.
The recommended coverage values should be followed to ensure the best protection ability.
Applicable national health and safety precautions must be followed in the pre-treatment and coating of substrates containing asbestos.
Protect the surfaces not to be painted.

Mechanical stress can cause lighter visible spots, in particular, in darker painted surfaces. This is a typical feature for all matt facade paints which does not, however, affect the product’s technical performance.
Cleaning of tools Wash the tools with water. Tikkurila Tool Cleaner is recommended for the removal of hardened paint.
Maintenance instructions Clean the surface cautiously with pressure washing without detergent at the earliest 1 month after painting. The washing may leave a permanent mark, therefore the area should be delimited imperceptible according to the structure lines. Remove dry loose dirt lightly with a soft brush without scrubbing. Tikkurila Mould Removal can be used to remove algae and mould, rinse off well.
Note: The surface needs always to be recoated after mould wash.
Maintenance treatment Surfaces painted with Finngard 500 can be re-painted with Finngard 150, Finngard 500 and Finngard Silicone Resin Paint.
EU VOC 2004/42/EC-limit value (Cat A/c) 40g/l(2010)
Finngard 500 contains VOC max. 40g/l.

HEALTH AND SAFETY LABELLING
according to Regulation (EC) No. 1272/2008
The product is not classified as dangerous. A Safety Data Sheet is available on request.Safety data sheet

DECLARATION OF PERFORMANCE Declaration of Performance EN1504-2

ENVIRONMENTAL and WASTE DISPOSAL Empty cans should be recycled or disposed of in accordance with local regulations. Liquid waste should be destroyed according to the local regulations.
TRANSPORT ADR: not classified
sre261113 / jar270212 / ome171110 / klu270613 / 574-s


CE
Product for protection and repair of concrete structures – Coating
CE logo
0809
Tikkurila Oyj
Kuninkaalantie 1
FI-01300 Vantaa, Finland
13
0809-CPD-0773
EN 1504-2:2004
Product for protection and repair of concrete structures – Coating
Release of dangerous substances
NPD
Permeability to CO2
CO2sD > 50 m
Permeability to water vapour
class I, sD < 5 m
Water permeability
w < 0.1 kg/m² ∙ h0,5
Adhesion strength by pull off test
≥ 1,0 N/mm²
Reaction to fire
F (NPD)