PRODUCT DATA SHEET
|DESCRIPTION||A two component, amine adduct cured epoxy finish.|
|PRODUCT FEATURES||Used especially as a finishing coat in epoxy systems exposed to heavy abrasion and/or chemical stress. Also suitable for concrete floors.|
|RECOMMENDED USES||Recommended for bridges, tanks and different types of steelwork and equipment in the wood processing and chemical industries, such as tubular bridges, conveyors, paper machines etc.|
|Features||Withstands +150 ºC dry heat and + 60 ºC in immersion. Withstands immersion in dilute solutions of non-oxidizing acids, alkalis and salts. Resists only temporary splashes of oxidizing acids and bleaching solutions. Withstands chemically active gases and dust. Withstands immersion in mineral/vegetable/animal fats and oils.|
|Colour Cards||RAL, NCS, SSG, BS, MONICOLOR NOVA and SYMPHONY colour cards. TEMASPEED tinting.|
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
|Mixing ratio||Base 3 parts by volume 170-series.
Hardener 1 part by volume 008 7580
|Application method||By airless spray or brush.|
|Pot-life (+23°C)||5 hours|
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
|Solids volume||55 ± 2 volume % (ISO 3233)
68 ± 2 weight %
|Density||1.3 - 1.4 kg / l (mixed) depending on colour.|
|Application conditions||All surfaces must be dry. The temperature of the ambient air, surface or paint should not fall below +10 ºC during application or drying. Relative humidity should not exceed 80 %. The surface temperature of the steel should remain at least 3 ºC above the dew point.|
|Preparation||Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)
Concrete surfaces: The surface must be dry and at least 4 weeks old. The relative humidity of the concrete should not exceed 97%. Remove any splashes and unevennesses by grinding. Remove laitance and form oil from concrete castings by sanding or blast cleaning. Any cracks, crevices and voids must be repaired with a mixture of TEMAFLOOR 200 and fine dry quartz sand.
|Priming||TEMACOAT GPL-S PRIMER, TEMACOAT GF PRIMER, TEMACOAT HB PRIMER, TEMACOAT PM PRIMER, TEMACOAT GPL-S MIO, TEMACOAT SPA, TEMALINE LP PRIMER, TEMAMASTIC PM 100, TEMABOND and FONTECOAT EP PRIMER.|
|Painting||By airless spray or brush. At spray application the paint should be thinned 5 - 15 %. Airless spray nozzle tip 0.011" - 0.017" and nozzle pressure 120 - 160 bar. Spray angle shall be chosen according to the shape of the object.
At brush application the paint can be thinned according to the circumstancies.
|Mixing of components||First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use Temaspeed Squirrel Mixer for mixing.|
|Cleaning of tools||Thinner 1031.|
|EU VOC 2004/42/EC-limit value||The Volatile Organic Compounds amount is 430 g/litre of paint mixture.
VOC content of the paint mixture (thinned 15 % by volume) is 495 g/l.
|HEALTH AND SAFETY CLASSIFICATION|
|Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oy.|
|Product safety data sheet||TEMACOAT GPL [GB-ENG]|
|Thinner safety data sheet||THINNER 1031 [GB-ENG]|
|Hardener safety data sheet||TEMACOAT GPL HARDENER [GB-ENG]|