Temacoat SPA 50

A two-component, resin-modified epoxy paint. It is mostly used for indoors and outdoors steel constructions. 



The paint is solvent-borne
The coverage of the paint on rough surfaces
4.5
m2/l
The coverage of the paint on smooth surfaces
8.5
m2/l

Good adhesion to various surfaces

Can be applied to steel, zinc and aluminium. Rapidly recoatable and ready to handle paint. It is also suitable as a single-coat system.

Good mechanical and chemical resistance

Forms durable film with good mechanical, chemical and climatic resistant properties. Excellent as a primer, intermediate or finish coat on surfaces exposed to stress.


Temacoat SPA 50 is mostly used for





Paint and coating systems for metal industries


PRODUCT DATA SHEET
22.10.2009

Temacoat SPA 50 - Epoxy paint

 
Temacoat SPA50
DESCRIPTION A two-component resin-modified epoxy paint.
PRODUCT FEATURES Good adhesion to steel, zinc and aluminium surfaces. Used as a primer, intermediate or finish coat on surfaces exposed to climatic, mechanical and chemical stress. Also suitable as a single coat system.
Recommended uses Recommended for building frameworks, tubular bridges, conveyors and other steelwork and equipment.

TECHNICAL DATA
Colour Cards RAL, NCS, SSG, BS, MONICOLOR NOVA and SYMPHONY colour cards. TEMASPEED tinting.
Gloss groups Semi-gloss
Coverage

Recommended film thicknesses

Theoretical coverage

dry

wet

 

80 µm

115 µm

8.5 m2/l

150 µm

215 µm

4.5 m2/l

 

Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Thinner 1031
Mixing ratio Base 4 parts by volume 158-series
Hardener 1 part by volume 008 5607
Application method By airless spray or brush.
Pot-life (+23°C) 6 hours
Drying times

DFT 100 µm

0 ºC

+ 10 ºC

+ 23 ºC

+ 35 ºC

Dust dry, after

16 h

4 h

2 h

1 h

Touch dry, after

24 h

10 h

4 h

2 h

Recoatable, min. after

24 h

3 h

1 h

½ h

Recoatable, surfaces to be submerged,  min. after

4 d

28 h

12 h

6 h

Recoatable with polyurethane paints, min. after

1 d

5 h

2 h

1 h


Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Solids volume 68 ± 2 volume % (ISO 3233)
81 ± 2 weight %
Density 1.4 - 1.5 kg / l (mixed)
Product code 158-series

APPLICATION DETAILS
Application conditions All surfaces must be clean and dry and free from contamination. The temperature of the substrate should be minimum 0 °C and at least 3 ° C above the dew point of the air. The product should not be applied at temperatures below 0 °C where there is a possibility of ice formation on the substrate. The temperature of paint itself should be above + 15 °C for proper application. Good ventilation is required in confined areas during application and drying.

Note! There is a natural tendency of epoxy coatings to chalk and discolor on exterior exposure.
Preparation Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)

Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.

Zinc surfaces: Sweep blast clean with mineral abrasives, e.g. quartz sand, to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with PANSSARIPESU detergent.

Hot dip galvanized surfaces are recommended to be painted with a mist coat (paint thinned 25 - 30 %) before the actual priming.

Aluminium surfaces: Sweep blast clean with non-metallic abrasives to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with MAALIPESU detergent.

Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)
Priming Temacoat SPA Primer, Temazinc 77, Temazinc 88 and Temazinc 99.
Finishing Temacoat HB 30, Temacoat GPL, Temacoat GS 50, Temacoat GPL-S MIO, Temacoat SPA 50, Temadur and Temathane.
Painting By airless spray or brush. At spray application the paint should be thinned 0 - 10 % by volume. Airless spray nozzle tip 0.015" - 0.021" and nozzle pressure 120 - 180 bar. Spray angle shall be chosen according to the shape of the object. At brush application the paint should be thinned according to the circumstancies.
Mixing of components First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use mechanical mixer for mixing.
Cleaning of tools Thinner 1031.
EU VOC 2004/42/EC-limit value The Volatile Organic Compounds amount is 300 g/litre of paint mixture.
VOC content of the paint mixture (thinned 30 % by volume) is 420 g/l.

HEALTH AND SAFETY LABELLING
according to Regulation (EC) No. 1272/2008
Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oy.
Safety data sheetTemacoat SPA 50
Thinner safety data sheetTemacoat SPA 50
Hardener safety data sheetTemacoat SPA 50
 
-


Back

Counter for metal coatings

Tikkurila offers wide range of paints and coatings for metal surfaces for different conditions, applications and needs. Tikkurila cost comparison program calculates costs and helps to find the best solution for your project.

VOC counter for metal coatings

Tikkurila VOC calculation program is based on VOC Directive 1999/13/EC valid in the whole EC area, which is aimed to reduce VOC emissions in different industrial activities. The calculation program is meant to be used as a preliminary mapping of solvent emissions.