Temalac SC-F 40

A high-solids alkyd paint, that used as a single-coat for interior and exterior steel surfaces.

The paint is solvent-borneTool: spray
The coverage of the paint on rough surfaces
5.1
m2/l
The coverage of the paint on smooth surfaces
6.1
m2/l

Contains anti-corrosive pigments

Temalac SC-F 40 is an alkyd paint, that contains anti-corrosive pigments and can be used as a single-coat system.

High film-building properties 

Temalac SC-F 40 has good application properties and can be applied up to 160µm wet film without sagging.


Temalac SC-F 40 is mainly used for:




PRODUCT DATA SHEET
11.03.2013

Temalac SC-F 40 - Alkyd paint

 
Temalac SC-F 40
DESCRIPTION A high-solids alkyd paint, containing anti-corrosive pigments.
PRODUCT FEATURES
Recommended uses Recommended for steel framework, service platforms and different types of machinery and equipment.

TECHNICAL DATA
Features Recommended as a single coat system for steel surfaces both indoors and outdoors. Good application properties. High film build.
Colour Cards RAL, NCS, SSG, BS, MONICOLOR NOVA, SYMPHONY, TEMASPEED Tinting
Gloss groups Semi-gloss
Coverage

Recommended film thicknesses

Theoretical coverage

dry

wet

 

100 µm

160 µm

6,1 m2/l

120 µm

200 µm

5,1 m2/l

 

Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Thinner 1006
Application method By airless or conventional spray.
Drying times

DFT 80 µm

+ 10 ºC

+ 23 ºC

+ 35 ºC

Dust dry, after

30 min

20 min

10 min

Touch dry, after

8 h

5 h

3 h

Recoatable, after

2 weeks

1 week

1 week

 

Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Solids volume 61 ± 2 %. (ISO 3233)
76 ± 2 %.
Density 1.5 kg / l depending on colour.
Product code 617-series.

APPLICATION DETAILS
Application conditions All surfaces must be dry. The temperature of the ambient air, surface or paint should not fall below + 5 ºC during application or drying. Relative humidity should not exceed 80 %. The surface temperature of the steel should remain at least 3 ºC above the dew point.
Preparation Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)

Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1). If blast cleaning is not possible, use phosphating on cold rolled steel.

Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)
Priming Temalac SC-F 40
Finishing Temalac SC-F 40
Painting By airless or conventional spray. Mix the paint thoroughly before use. At airless spray application the paint should be thinned 0 - 5 % and at conventional spray application
5 - 10 %. Airless spray nozzle tip 0.011" - 0.015" and nozzle pressure 160 - 200 bar. Spray angle shall be chosen according to the shape of the object. In order to reach thicker coats use "wet-on-wet" technique.
Cleaning of tools Thinner 1006.
EU VOC 2004/42/EC-limit value The Volatile Organic Compounds amount is 360 g/litre of paint.
VOC content in ready to use paint (thinned 10 % by volume) is 410 g/l.
For industrial and professional use only.

HEALTH AND SAFETY LABELLING
according to Regulation (EC) No. 1272/2008
Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oyj.
Safety data sheetTemalac SC-F 40
Thinner safety data sheetTemalac SC-F 40
 
-


Back