PRODUCT DATA SHEET
07.06.2017
(Previous date 22.02.2010)

Temazinc 77 - Zinc-rich epoxy paint

 
Temazinc 77
DESCRIPTION A two-component, polyamide-cured zinc-rich epoxy paint.
PRODUCT FEATURES Used as a primer in epoxy, polyurethane, acrylic and chlorinated rubber systems for steel surfaces exposed to severe climatic conditions. Can be used without a topcoat on surfaces exposed to weathering.
Recommended uses Recommended for bridges, cranes and steel frameworks as well as steelwork and equipment in the forest and chemical industries, such as tubular bridges, conveyors etc.

TECHNICAL DATA
Features Offers cathodic protection of steel. The zinc content fulfils the requirements of ISO 12944-5.
Colour Range Grey.
Gloss groups Matt
Coverage

Recommended film thicknesses

Theoretical coverage

dry

wet

 

40 µm

75 µm

13.0 m2/l

80 µm

155 µm

6.5 m2/l


Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Thinner 1031
Mixing ratio Base 3 parts by volume 008 7405
Hardener 1 part by volume 008 7440
Application method By airless spray or brush.
Pot-life (+23°C) 16 hours
Drying times

DFT 40 µm

+ 5 ºC

+ 10 ºC

+ 23 ºC

+ 35 ºC

Dust dry, after

50 min

20 min

10 min

5 min

Touch dry, after

2 h

1 h

30 min

15 min

Recoatable, after

5 h

3 h

1 h

30 min


Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Solids volume 52 ± 2 % volume (ISO 3233)
Density 2.0 kg / l (mixed)
Product code Base paint 008 7405, Hardener 008 7440.

APPLICATION DETAILS
Application conditions All surfaces must be clean, dry and free from contamination. The temperature of the ambient air, surface and paint should not fall below +5ºC during application and drying. Relative humidity of the air should not exceed 80% during application and drying.
The surface temperature of steel should remain at least 3°C above the dew point.
Good ventilation and sufficient air movement is required in confined areas during application and drying.
Preparation Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)

Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1) In order to get the best performance the surface profile should be medium grit. (ISO 8503-2)
Finishing Temacoat GPL-S Primer, Temacoat GF Primer, Temacoat GPL-S MIO, Temacoat GS 50, Temacoat RM 40, Temacoat HB 30, Temacoat SPA, Temabond, Temachlor 40, Temacryl AR 50 and Temanyl MS Primer.
Painting For airless spraying, the product is thinned depending on the temperature of the components and shape of the object approximately 0–5%. Agitate during application. Recommended nozzle tip is 0.015"–0.021" and pressure 120–180 bar. Spray angle shall be chosen according to the shape of the object.

For brush application the paint should be thinned according to the circumstancies.

Sharp edges, corners, weld seams and other areas difficult to cover properly by spray application should be coated by brush before the spray application.
Mixing of components First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use power mixer for mixing. Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface and weaken the properties of the coating.
Cleaning of tools Thinner 1031.
EU VOC 2004/42/EC-limit value The Volatile Organic Compounds amount is 480 g/litre of paint.
VOC content of the paint mixture (thinned 5% by volume) is 495 g/l.

For industrial use only.

HEALTH AND SAFETY LABELLING
according to Regulation (EC) No. 1272/2008
Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oyj.