PRODUCT DATA SHEET
(Previous date 30.08.2012)
Duasolid 50 - Oxirane-ester paint
|DESCRIPTION||A two-component oxirane-ester paint containing active anti-corrosive pigments.|
|PRODUCT FEATURES||Used as a single coat or as a topcoat in oxirane ester based systems on steel surfaces exposed to abrasion and chemicals in severe climatic conditions.|
|Recommended uses||Suitable for earth moving machines, haulage and lifting equipment, forklifts, agricultural machinery, electric appliances, pumps and other steel structures, equipment and machinery.|
|Features||Excellent durability. Environmentally more friendly and for users more safe alternative than epoxy and polyurethane paints. High volume solids. High film build properties, up to 100 µm / one coat.|
|Colour Cards||RAL, NCS, SSG, BS, MONICOLOR NOVA and SYMPHONY colour cards. TEMASPEED tinting. Gloss varies depending on the used hardener. See application.|
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
|Thinner||1048 and 1112|
|Mixing ratio||Base 2 parts by volume 527-series
Hardener 1 part by volume 008 7675, other hardeners: see application
|Application method||By airless, conventional or electrostatic spray|
|Pot-life (+23°C)||8 hours|
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
|Solids volume||approx. 65 ± 2 volume %
|Density||approx. 1.5 kg / l|
|Application conditions||All surfaces must be dry. The temperature of the ambient air, surface or paint itself should not fall below +10 ºC during application or drying. Relative humidity should not exceed 80 %. The surface temperature of the steel should remain at least 3 ºC above the dew point.|
|Preparation||Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)
Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.
Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)
|Priming||Duasolid Primer and Duasolid 50.|
|Painting||By airless, conventional or electrostatic spray. At airless spray application the paint can be thinned if necessary to a viscosity of 30–60 s DIN 4. Airless spray nozzle tip
"0.011–0.015", pressure ratio at least 30:1 and nozzle pressure 120–180 bar.
At conventional spray application the viscosity should be 20–40 s DIN 4 and at electrostatic spraying 20–40 s DIN 4.
Properties and gloss of DUASOLID 50 will vary according to the used hardener:
Hardener 008 7675 gloss abt. > 70 mixing ratio 2:1
Hardener 008 7665 gloss abt. 60 mixing ratio 2:1
Hardener 008 7667 gloss abt. 10 mixing ratio 2:1
Hardener 008 7672 gloss abt. 40 mixing ratio 2:1
Hardener 008 7668 gloss abt. < 10 mixing ratio 2:1
Avoid hot spray!
|Mixing of components||First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use Temaspeed Squirrel Mixer for mixing.|
|Cleaning of tools||Thinner 1048 or Thinner 1112.|
|EU VOC 2004/42/EC-limit value||The Volatile Organic Compounds amount is 320 g/litre of paint mixture.
VOC content of the paint mixture (thinned 15 % by volume) is 399 g/l.
|HEALTH AND SAFETY LABELLING|
according to Regulation (EC) No. 1272/2008
|Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oyj.|
|Safety data sheet||DUASOLID 50 [GB-ENG]|
|Thinner safety data sheet||Duasolid 50|
|Hardener safety data sheet||Duasolid 50|