PRODUCT DATA SHEET
Temacoat GPL - Epoxy finish
|DESCRIPTION||A two-component, amine-adduct cured epoxy finish.|
Used especially as a finishing coat in epoxy systems exposed to heavy abrasion and/or chemical stress. Due to CE marking also suitable for concrete surfaces.
|Recommended uses||Recommended for bridges, tanks and different types of steelwork and equipment in the wood processing and chemical industries, such as tubular bridges, conveyors, paper machines etc.|
|Features||Withstands +150 ºC dry heat and +60 ºC in immersion. Withstands immersion in dilute solutions of non-oxidizing acids, alkalis and salts. Resists only temporary splashes of oxidizing acids and bleaching solutions. Withstands chemically active gases and dust. Withstands immersion in mineral/vegetable/animal fats and oils.|
|Colour Cards||RAL, NCS, SSG, BS, MONICOLOR NOVA and SYMPHONY colour cards. TEMASPEED tinting.|
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
|Mixing ratio||Base 3 parts by volume 170-series.
Hardener 1 part by volume 008 7580
|Application method||By airless spray or brush.|
|Pot-life (+23°C)||5 hours|
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
|Solids volume||55 ± 2 volume % (ISO 3233)
68 ± 2 weight %
|Density||1.3 - 1.4 kg / l (mixed) depending on color.|
|Application conditions||All surfaces must be clean, dry and free from contamination. The temperature of the ambient air, surface and paint should not fall below +10ºC during application and drying. Relative humidity of the air should not exceed 80% during application and drying. The surface temperature of steel should remain at least 3°C above the dew point.
Good ventilation and sufficient air movement is required in confined areas during application and drying.
Note! There is a natural tendency of this coating to chalk, discolor or yellow unevenly. It is recommended to use polyurethane topcoat when there are high aesthetical requirements on color appearance.
|Preparation||Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)
Concrete surfaces: The surface must be dry and at least 4 weeks old. The relative humidity of the concrete should not exceed 97%. Remove any splashes and unevennesses by grinding. Remove laitance and form oil from concrete castings by sanding or blast cleaning. Any cracks, crevices and voids must be repaired with a mixture of Temafloor 200 and fine dry quartz sand.
|Priming||Temacoat GPL-S Primer, Temacoat GPL-S MIO, Temacoat SPA and Temabond.|
|Painting||For airless spraying, the product is thinned approximately 0–10%. Recommended nozzle tip is 0.011"–0.017" and pressure 120–160 bar. Spray angle shall be chosen according to the shape of the object.
For brush application the product should be thinned according to the circumstancies.
|Mixing of components||First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use mechanical mixer for mixing.|
|Cleaning of tools||Thinner 006 1031.|
|EU VOC 2004/42/EC-limit value||The Volatile Organic Compounds amount is 455 g/litre of paint mixture.
VOC content of the paint mixture (thinned 10 % by volume) is 495 g/l.
|HEALTH AND SAFETY LABELLING|
according to Regulation (EC) No. 1272/2008
|Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oyj.|
|Safety data sheet||Temacoat GPL|
|Thinner safety data sheet||Temacoat GPL|
|Hardener safety data sheet||Temacoat GPL|
|The European harmonized productstandard EN 1504-2:2004 defines the requirements for surface protection systems for concrete.
This product is tested and CE-labelled in accordance with the tables 1d, 1f and 1g in the
|Declaration of performance: TIK-0170-5001|