PRODUCT DATA SHEET
Temadur SC-F 80 - Polyurethane paint
|DESCRIPTION||A two-component fast-drying gloss polyurethane paint, containing anti-corrosive pigments, hardener aliphatic isocyanate.|
Recommended especially to be used as a single coat finish for agricultural and earth moving machinery and other machinery and equipment. Also suitable to be used as a topcoat in epoxy/polyurethane systems exposed to weathering and chemical stress, e.g. storage tank exteriors, steel framework and other steel structures.
|Recommended uses||Storage tank exteriors, steel framework and other steel structures.|
|Features||Excellent weathering and abrasion resistance. A durable, easy to clean and non-chalking topcoat with good gloss and colour retention.|
|Colour Cards||RAL, NCS, SSG, BS, MONICOLOR NOVA and SYMPHONY colour cards. TEMASPEED tinting.|
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
|Thinner||1048 and 1067|
|Mixing ratio||Base 4 parts by volume 586 serie
Hardener 1 part by volume 008 7640
By airless or conventional spray.
|Pot-life (+23°C)||app. 1 hour|
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation. When forced drying in temperatures +50–+100ºC, use flash-off time between 5–30 minutes, depending on the wet film thickness and the actual temperature.
|Solids volume||65 ± 2 % volume (ISO 3233)
80 ± 2 % weight
|Density||1.4 ± 0.1 kg / l (mixed)|
|Product code||586 series|
|Application conditions||All surfaces must be dry. The temperature of the ambient air, surface or paint should not fall below +5ºC during application or drying. Relative humidity should not exceed 80%. The surface temperature of the steel should remain at least 3ºC above the dew point.|
|Preparation||Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)
Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.
Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)
|Priming||Temadur 20, Temacoat GPL-S Primer, Temacoat Primer, Temacoat GPL-S MIO, Temabond and Temanyl PVB.|
|Finishing||Temadur and Temathane.|
|Painting||By airless or conventional spray.
Airless spray: depending on the temperature of the components and shape of the object the paint can be thinned 0–15 %. Airless spray nozzle tip 0.011"–0.015" and nozzle pressure 160–200 bar. Spray angle shall be chosen according to the shape of the object. In order to reach thicker coats (over 100 µm) use always "wet-in-wet" technique.
At conventional spray the paint should be thinned 15–18 % to a viscosity of
|Mixing of components||First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use Temaspeed Squirrel Mixer for mixing.|
|Cleaning of tools||Thinner 1067 or Thinner 1048.|
|EU VOC 2004/42/EC-limit value||The Volatile Organic Compounds amount is 320 g/litre of paint.
VOC content in paint (thinned 18 % by volume) is 420 g/l.
|HEALTH AND SAFETY LABELLING|
according to Regulation (EC) No. 1272/2008
|Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oyj.|
|Safety data sheet||Temadur SC-F 80|
|Thinner safety data sheet||Temadur SC-F 80|
|Hardener safety data sheet||Temadur SC-F 80|