Temasil 90 - Silicate zinc-rich paint

Temasil 90
DESCRIPTION A two-component, ethyl-silicate zinc-rich paint.
PRODUCT FEATURES Can be used as a single coat or as a primer in protective coating systems.
Recommended uses Recommended for bridges, pipework, heat exchangers and chemical tanks etc.

Features Offers cathodic protection of steel. Excellent resistance to abrasion and weathering. Excellent resistance also to high, dry temperatures up to + 480 ºC. Withstands immersion in oils and various solvents. Separate chemical resistance table available.
Colour Range Greenish grey.
Gloss groups Matt

Recommended film thicknesses

Theoretical coverage




60 µm

120 µm

9.2 m2/l

80 µm

160 µm

6.9 m2/l

Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Thinner 1029
Mixing ratio Base 1 part by volume 008 7381
Hardener 1 part by volume 008 7380
Application method By airless or conventional spray or brush.
Pot-life (+23°C) 5 hours
Drying times

DFT 75 µm

+ 10 ºC

+ 23 ºC

+ 35 ºC

Dust dry, after

½ h

15 min

10 min

Touch dry, after

1 h

½ h

15 min

Recoatable, RH 85 % *see overleaf, after

36 h

5 h

2 h

Recoatable, RH 70 %, after

48 h

24 h

7 h

Recoatable, RH 50 %, after


48 h

24 h

Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Solids volume 55 ± 2 % volume
Density 2.0 kg / l (mixed)
Product code 008 7381

Application conditions All surfaces must be dry. The temperature of the ambient air or surface should not fall below -15 ºC during application and drying. Relative humidity should be 50 - 90 %. The surface temperature of the steel should remain at least 3 ºC above the dew point.
Preparation Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)

Steel surfaces: Blast clean to grade Sa2½ - 3. (ISO 8501-1)
Finishing Temachlor 40, Temacryl AR, Temacryl EA, Temal, Temacoat GPL-S Primer, Temacoat GPL-S MIO, Temacoat RM 40 and Temacoat SPA.

Temasil 90 may be overcoated with above mentioned paints when Thinner 1029 does not dissolve the coat. Before overcoating it is recommended to spray a misty coat with 25 % thinned Temacoat GS 50.
Painting By airless or conventional spray or brush. Agitate during application. Depending on the application method the paint can be thinned 0 - 5 % by volume. Airless spray nozzle tip 0.018" - 0.021" and nozzle pressure 120 - 180 bar. Spray angle shall be chosen according to the shape of the object.

When coating interiors of chemical tanks or working in dry conditions, it is recommended to rinse the paint film with fresh water 1 - 24 hours after application. Sharp edges, corners, weld seams and other areas difficult to cover properly by spray application should be coated by a brush before the spray application.

Note! There is a risk of mudcracking or peeling with heavier coats than approx. 100 µm dry film thickness.

Separate application instructions available.
Mixing of components First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use Temaspeed Squirrel Mixer for mixing.
Cleaning of tools Thinner 1029.
EU VOC 2004/42/EC-limit value The Volatile Organic Compounds amount is 470 g/litre of paint.
VOC content of the paint mixture (thinned 5 % by volume) is 480 g/l.

according to Regulation (EC) No. 1272/2008
Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oy.
Safety data sheetTemasil 90
Thinner safety data sheetTemasil 90
Hardener safety data sheetTemasil 90